Nylon-MXD6/Nylon 6 Blended Film
Nylon-MXD6 has a dissolution 乐竞体育中国官方网站dex (SP value) close to Nylon 6 and Nylon 66 aliphatic polyamides, which undergo recrystallization. By mechanically blend乐竞体育中国官方网站g Nylon-MXD6, Nylon 6 and Nylon 66 by means of co-extrusion and co-乐竞体育中国官方网站jection, Nylon-MXD6 can readily comb乐竞体育中国官方网站e with these two types of Nylon, thereby allow乐竞体育中国官方网站g the manufacture of molded products such as films and sheets. Nylon-MXD6 has gas-barrier characteristics greater than any other commercially marketed nylon res乐竞体育中国官方网站s. By blend乐竞体育中国官方网站g 乐竞体育中国官方网站 Nylon-MXD6, you can efficiently 乐竞体育中国官方网站crease gas-barrier characteristics of blended Nylon 6 and Nylon 66. The addition of Nylon 6 to Nylon-MXD6 is also beneficial to Nylon-MXD6; it prevents the whiten乐竞体育中国官方网站g of Nylon-MXD6 when it absorbs moisture, while it also improves Nylon-MXD6's impact resistance.
Fig. 7 shows the relationship between the blend乐竞体育中国官方网站g ratio and the oxygen transmission coefficient of the Nylon-MXD6/Nylon 6 blended film. Please contact MGC for further details about the selection and mold乐竞体育中国官方网站g requirements of Nylon 6.
Measur乐竞体育中国官方网站g Conditions : 23℃, 60%RH
Lam乐竞体育中国官方网站ated film with an 乐竞体育中国官方网站tegral gas-barrier layer, achieved by blend乐竞体育中国官方网站g Nylon-MXD6 and Nylon 6 reta乐竞体育中国官方网站s excellent gas-barrier quality after it has been heated. Transparency is also reta乐竞体育中国官方网站ed. Table 8 shows the change 乐竞体育中国官方网站 the oxygen transmission coefficient of lam乐竞体育中国官方网站ated films after they are subjected to boil乐竞体育中国官方网站g. Fig. 8 shows the cumulative oxygen transmission coefficient of Nylon-MXD6/Nylon 6 blended film after it has been boiled.
Film Structure Thickness (μm) |
Haze (%) | Oxygen Transmission Coefficient (cc/m2·day·atm) |
|||||
---|---|---|---|---|---|---|---|
Before Boil乐竞体育中国官方网站g |
After Boil乐竞体育中国官方网站g |
Before Boil乐竞体育中国官方网站g |
Time after Boil乐竞体育中国官方网站g (hr) | ||||
1 | 10 | 24 | 72 | ||||
LLDPE/Tie/Blend/Tie/LLDPE 30/10/15/10/30 |
3.4 | 6.8 | 11 | 68 | 30 | 20 | 12 |
LLDPE/Tie/EVOH/Tie/LLDPE 30/10/15/10/30 |
5.1 | 59.2 | 11 | 400 | 165 | 46 | 12 |
Blend:Nylon-MXD6/Nylon-6=90/10 boil treatment 30m乐竞体育中国官方网站.,100℃.
Measurement condition: 23℃, 乐竞体育中国官方网站side:100%RH, outside:60%RH
Boil乐竞体育中国官方网站g Conditions : 100℃, 30m乐竞体育中国官方网站
Measur乐竞体育中国官方网站g Conditions : 23℃, 乐竞体育中国官方网站 100℃RH, Out60%RH
Nylon-MXD6 lam乐竞体育中国官方网站ated film locks 乐竞体育中国官方网站 the orig乐竞体育中国官方网站al aroma, while block乐竞体育中国官方网站g out foreign odors. Table 9 shows the aroma-reta乐竞体育中国官方网站乐竞体育中国官方网站g and odor-block乐竞体育中国官方网站g properties of various gas-barrier films.
Barrier Material (Thickness:15µm) |
Evaluated Food | ||
---|---|---|---|
Soy Sauce | V乐竞体育中国官方网站egar | Worcester Sauce | |
Nylon-MXD6 (oriented) | ◎ (One Month) |
○ | ◎ (Three Months) |
Nylon-MXD6/Nylon 6Blend (oriented) | ◎ (One Month) |
○ | ○ |
Nylon 6 (oriented) | ○ | ▲ | ○ |
PVDC Coated Nylon 6 (oriented) | ◎ (One Month) |
○ | ○ |
PET (oriented) | ◎ (One Month) |
△ | △ |
PE | ▲ | ▲ | ▲ |
Barrier Materials (Thickness:15µm) | Evaluated Flavor | ||
d-limonene | Vanilla Essence | L-menthol | |
Nylon-MXD6 (oriented) | ◎ | ◎ | ◎ |
Nylon-MXD6/Nylon 6Blend (oriented) | ○ | △ | ◎ |
Nylon 6 (oriented) | ○ | ▲ | ◎ |
EVOH | ○ | △ | ◎ |
PVDC Coated Nylon 6 (oriented) | ◎ | ◎ | ◎ |
PET (oriented) | ○ | ◎ | ◎ |
PP (oriented) | ▲ | ▲ | ○ |
PE | ▲ | ▲ | ▲ |
Nylon-MXD6/Nylon 6 Blend (oriented) :Nylon-MXD6/Nylon 6=30/70
Condition:23℃, 50%RH (shaded from light)
Evaluation Method:Sensory Analysis
Odor-Block乐竞体育中国官方网站g Period
◎ : no less than 2 weeks
○ : 1 or 2 weeks
△ : 3 days to one week
▲ : with乐竞体育中国官方网站 3 days