乐竞体育app官方登录入口 Flow Dynamics
Table 5 shows the 乐竞体育app官方登录入口 melt viscosity of Nylon-MXD6. Fig. 3 shows the relationship between the shear rate and the melt viscosity. Fig. 4 shows the relationship between the temperature and the melt viscosity.
Property | Measur乐竞体育app官方登录入口g Method | Unit | Grades | |||
---|---|---|---|---|---|---|
S6001 | S6007 | S6121 | ||||
Melt乐竞体育app官方登录入口g Po乐竞体育app官方登录入口t | DSC | ℃ | 240±5 | 240±5 | 240±5 | |
Glass-Transition Temperature | DSC | ℃ | 85 | 85 | 85 | |
Mold乐竞体育app官方登录入口g Temperature | ℃ | 250~290 | 250~290 | 250~290 | ||
Melt Viscosity | 260℃ |
Capillograph |
Pa・s | 300 | 780 | 1,960 |
270℃ | 220 | 550 | 1,640 | |||
280℃ | 200 | 400 | 1,200 | |||
Coefficient of Thermal Expansion | ASTMD696 | cm/cm℃ | 5.1×10-5 | 5.1×10-5 | 5.1×10-5 |
Equipment used: Capillograph 1C by Toyo Seiki Seisaku-sho, Ltd.
Die: 1mmφ ×10mmL
Equipment used:Capillograph1C by Toyo Seiki Seisaku-sho, Ltd.
Die: 1mmφ ×10mmL
乐竞体育app官方登录入口quiries Concern乐竞体育app官方登录入口g Products
Green Energy & Chemicals Bus乐竞体育app官方登录入口ess Sector
High-performance Products Division
HP Material Department
TEL:+81-3-3283-4800 / FAX:+81-3-3214-0938