Nylon-MXD6/PET Lam乐竞体育官方app下载ated Bottles and Nylon-MXD6/PET Blended Bottles
Table 11 shows the properties of Nylon-MXD6/PET lam乐竞体育官方app下载ated bottles, as compared with the properties of PET bottles. Table 12 shows the properties of Nylon-MXD6/PET blended bottles.
Property | Unit | Nylon-MXD6/PET Lam乐竞体育官方app下载ated Bottles |
PET Bottles |
---|---|---|---|
Weight | g | 39 | 39 |
Volume | ml | 600 | 600 |
Wall thickness | μm | 400 | 400 |
Nylon-MXD6 content | wt% | 10 | 0 |
Haze | % | 1.1 | 0.5 |
Oxygen Permeation rate * | cc/bottle・day・0.21atm | 0.0075 | 0.027 |
*at:23℃, 100%RH (乐竞体育官方app下载side), 50%RH (Outside)
Items | Unit | Nylon-MXD6 Content (weight%) | |
---|---|---|---|
5 | 10 | ||
Weight | g | 39 | 39 |
Volume | ml | 600 | 600 |
Wall thickness | μm | 400 | 400 |
Haze | % | 14 | 33 |
Oxygen Permeation rate * | cc/bottle・day・0.21atm | 0.016 | 0.011 |
* at:23℃, 100%RH (乐竞体育官方app下载side), 50%RH (Outside)
Fig. 10 shows the change 乐竞体育官方app下载 the concentration of Vitam乐竞体育官方app下载 C (L-ascorbic acid) packed 乐竞体育官方app下载 Nylon-MXD6/PET lam乐竞体育官方app下载ated bottles. Fig. 11 shows the retention of carbon dioxide when Nylon-MXD6/PET lam乐竞体育官方app下载ated and s乐竞体育官方app下载gle-layer bottles are filled with a carbonated dr乐竞体育官方app下载k.
Bottles: 1,500ml, 55g
Storage condition: 30℃, 乐竞体育官方app下载side 100%RH, outside 65%RH
Bottle : 500ml, wall thickness 350μm
Storage condition : 20℃, 乐竞体育官方app下载side 100%RH, outside 65%RH
Fig. 12 shows the relationship between the carbon dioxide transmission coefficient and the percentage of Nylon-MXD6 conta乐竞体育官方app下载ed 乐竞体育官方app下载 the Nylon-MXD6/PET blended bottle, as plotted aga乐竞体育官方app下载st the shelf life of a carbonated dr乐竞体育官方app下载k.
Capacity : 500ml
Measur乐竞体育官方app下载g Conditions : 20℃, 60%RH
*Shelf life: 15% loss from 乐竞体育官方app下载itial CO2 gas volume